Coke furnace silicon bricks are mainly used in the heat storage room, oblique road, charcoal room, combustion room, top of the furnace, and bottom of the furnace.
Brown corundum refractory brick is made of fused corundum as the main raw material. It is formed by high pressure and fired at high temperature. It has high thermal shock stability, low porosity, low expansion, good resistance to melt vapor and gas erosion, and excellent oxidation resistance. Dimensionally accurate advantages.
The high-alumina refractory bricks sold by Yuying refractory manufacturers are commonly used refractory bricks with high thermal stability and refractoriness above 1770°C. It has good slag resistance and is used for the lining of steelmaking electric furnaces, glass melting furnaces, cement rotary furnaces, etc.
Anchor bricks are anchor bricks for industrial kilns. The electric furnace roof is a furnace roof structure supported by metal hanging bricks and refractory bricks. Therefore, the leakage of reactive gas and hot gas in the furnace will damage the metal hanging parts, thereby causing furnace damage. roof collapse accident. Anchor bricks are also called hanging bricks and anchors.
Yuying Refractory produces a complete set of refractories for electrolyzers, and the new impermeable bricks are used in conjunction with impermeable castables
Anti stripping high alumina bricks are referred to as anti-stripping bricks or anti-stripping refractory bricks. Anti-stripping high-alumina bricks are widely used in my country's new dry process kiln, Libore kiln and wet process kiln, including kiln door cover, rising flue, cooling zone, decomposition zone, safety belt, transition zone, coolant rear Walls and side walls and beams with curved ceilings.
Magnesia chrome bricks are refractory products with magnesia (MgO) and chromium trioxide (Cr2O3) as the main components, and periclase and spinel as the main mineral components. The main raw materials for the manufacture of magnesia-chrome bricks are sintered magnesia and chromite.
Magnesia alumina bricks use periclase as the main crystal phase and magnesia-alumina spinel as the matrix. They are better in thermal shock resistance than magnesia bricks. In order to improve the thermal shock resistance of magnesia bricks, alumina or alumina is introduced into the ingredients. Bauxite clinker fine powder to form a magnesia-alumina sharp stone matrix, thereby making magnesia-alumina bricks
The alkali-resistant brick for cement kiln has the characteristics of strong alkali erosion resistance, good thermal shock resistance and high cost performance.
The heavy parts of the chrome-zirconium mullite composite bricks are made of high-purity sintered mullite, high-purity chromium oxide, high-purity zirconia, and Guangbai mud as the main raw materials, and the light part of the raw materials are made of 47 mullite, kyanite, Bleaching beads, coke gemstones and Guangxi white mud are the main raw materials
The heavy part of the raw materials for the chrome zirconium corundum composite brick is sintered tabular corundum, high-purity chromium oxide, high-purity zircon, and Guangxi white cement.As the main raw material, the light part of the raw material is made of 47 mullite, kyanite, floating beads and coke gemstones as the main raw materials. During molding, a separator is set in the middle of the mold, and heavy materials and light materials are added at both ends. After high pressure molding , finished products made of high temperature sintering.
Silica brick: an acidic refractory mainly composed of tridymite, cristobalite and a small amount of residual quartz and glass phases. Its silica content is more than 94%, it has anti-acid slag erosion performance, high high temperature strength, high load softening temperature, long-term use in high temperature flower wells without deformation, but low thermal shock stability (heat exchange in water is 1-4 Second-rate).