Anti stripping high alumina bricks are referred to as anti-stripping bricks or anti-stripping refractory bricks. Anti-stripping high-alumina bricks are widely used in my country's new dry process kiln, Libore kiln and wet process kiln, including kiln door cover, rising flue, cooling zone, decomposition zone, safety belt, transition zone, coolant rear Walls and side walls and beams with curved ceilings.
Magnesia chrome bricks are refractory products with magnesia (MgO) and chromium trioxide (Cr2O3) as the main components, and periclase and spinel as the main mineral components. The main raw materials for the manufacture of magnesia-chrome bricks are sintered magnesia and chromite.
Magnesia alumina bricks use periclase as the main crystal phase and magnesia-alumina spinel as the matrix. They are better in thermal shock resistance than magnesia bricks. In order to improve the thermal shock resistance of magnesia bricks, alumina or alumina is introduced into the ingredients. Bauxite clinker fine powder to form a magnesia-alumina sharp stone matrix, thereby making magnesia-alumina bricks
The alkali-resistant brick for cement kiln has the characteristics of strong alkali erosion resistance, good thermal shock resistance and high cost performance.
silicon mullite brick is a kind of refractory brick product made of super high alumina bauxite and silicon carbide as raw materials through a special sintering process. It has the characteristics of continuously forming a protective layer and reducing ring formation, and its heat resistance is also very good. The softening temperature under load can reach 1600 ℃, and the service life is long. Mainly used in the transition zone, decomposition zone and cooler of small and medium-sized cement kilns.
The heavy parts of the chrome-zirconium mullite composite bricks are made of high-purity sintered mullite, high-purity chromium oxide, high-purity zirconia, and Guangbai mud as the main raw materials, and the light part of the raw materials are made of 47 mullite, kyanite, Bleaching beads, coke gemstones and Guangxi white mud are the main raw materials
The heavy part of the raw materials for the chrome zirconium corundum composite brick is sintered tabular corundum, high-purity chromium oxide, high-purity zircon, and Guangxi white cement.As the main raw material, the light part of the raw material is made of 47 mullite, kyanite, floating beads and coke gemstones as the main raw materials. During molding, a separator is set in the middle of the mold, and heavy materials and light materials are added at both ends. After high pressure molding , finished products made of high temperature sintering.
Silica bricks for coke ovens are siliceous refractory products used for building coke ovens with tridymite as the main crystal phase. Coke oven silica bricks are used to build regenerator walls, ramps, combustion chambers, carbonization chambers and furnace roofs of coke ovens. Silica brick is an acid refractory material with good resistance to acid slag erosion. The softening temperature under load is as high as 1640-1670 °C, and the volume is relatively stable in long-term use at high temperature.
Silica brick: an acidic refractory mainly composed of tridymite, cristobalite and a small amount of residual quartz and glass phases. Its silica content is more than 94%, it has anti-acid slag erosion performance, high high temperature strength, high load softening temperature, long-term use in high temperature flower wells without deformation, but low thermal shock stability (heat exchange in water is 1-4 Second-rate).
High alumina brick is one of the indispensable basic refractory materials in the upper and middle parts of blast furnace body in iron and steel industry
Fireclay bricks are classified as weak acid refractories. Due to the large fluctuation range of chemical composition, different production methods, and differences in firing temperature, the properties of clay bricks change greatly.We can produce all kinds of Fireclay bricks according to customers' requirements
It is widely used in the lining of the kiln working face which is in direct contact with the flame, and has become one of the research hotspots in recent years.